High Thermal Conductivity Precision Zro2 Zirconia Ceramic Fixture Support

Product Description

High Thermal Conductivity Precision ZrO2 Zirconia Ceramic Fixture Support

The specification of ceramic parts

Material option	Zirconia (ZrO2),  Alumina(Al2O3), Silicon carbide(SiO2), Silicon nitride(Si3N4)
Forming methods	Dry pressed, Ceramic injection molding, Hot pressed, ISO pressed
Specification	OD can be from 1 to 50mm, length can be from 10mm to 800mm
Precision processing	CNC machining, Precision grinding, Polishing, Lapping,
Tolerance	The tolerance of OD and ID can be 0.001mm,  the tolerance of length can be 0.001mm
Key parameters	Roughness to be 0.02mm, Parallelism to be 0.001mm
Surface quality	Free of cracks, foreign contamination, mirror surface better than Ra0.1

The main features of zirconia ceramic parts
1.High density:  over 6 g/cm³, which makes it the densest body of the ceramic products
2.High hardness: over 9 on Mohs scale, diamond being 10, with a satin-smooth surface finish
3.High toughness: over 1200 MPa, approx. 4 times in comparison with 95% alumina
4. Excellent wear resistance, it's much better than aluminum oxide ceramics with longer life cycle
5. Low thermal conductivity:  less than 3 W/m.k at ambient temperature, so it's an ideal thermal material
6. Good chemical and corrosion resistance, it's equivalent to above 99% alumina

The description of zirconia ceramic parts
Zirconia ceramic parts are made of zirconium oxide ceramics which is a kind of strongest technical ceramic material with exceptional strength, high toughness, and superb reliability. These outstanding characteristics result in excellent resistance to wear and corrosion.

We have been offering a selection of partially stabilized zirconia, including Y-TZP( yttria-stabilized), MSZ ( magnesia stabilized ), CSZ- (ceria stabilized). Each stabilized zirconia provides unique and specific properties that meet the demands of extreme applications found in many industries.

With our production capability through CNC, precision grinding machines,  we are able to provide many different level precision zirconia ceramic parts to meet customers' high precision assembly needs.

The gallery of zirconia ceramic parts 
 

Datasheet of Technical ceramics

Property	Units	Material
		99.5% alumina	99% alumina	95% alumina	ZrO2 (Y-TZP)	ZrO2 (TTZ)
Density	g/cm^3	≥3.85	≥3.80	≥3.60	≥5.95	≥5.72
Water absorption	%	0	0	0	0	0
Hardness	HV	1700	1700	1500	1300	900
Flexural strength	Mpa	≥379	≥338	≥320	≥1200	≥1200
Compressive strength	Mpa	≥2240	≥2240	≥2000	≥1990	1750
Fracture toughness	Mpa m^1/2	4-5	4-5	3-4	6.5-8	11
Max. service temperature	ºC	1675	1600	1450	1000
CTE	1×10 ^-6/ºC	6.5~8.0	6.2~8.0	5.0~8.0	8.0~9.5	10.2
Thermal shock	T(ºC)	≥250	≥200	≥220	≥300	350
Thermal conductivity(25ºC)	W/m.k	30	29	24	3	3
Volume resistivity	ohm.cm
25ºC		>1 x 10^14	>1 x 10^14	>1 x 10^14	>1 x 10^11	>1 x 10^11
300ºC		1 x 10 ^12	8 x 10^11	10^12 -10^13	1 x 10 ^10	1 x 10 ^10
500ºC		5 x 10 ^10	2 x 10^9	1 x 10^9	1 x 10^6	1 x 10^6
Insulation strength	KV/mm	19	18	18	17	20
Dielectric constant(1Mhz)	(E)	9.7	9.5	9.5	29	28

 

Manufacturing flow chart of technical ceramic parts

We have in-housing comprehensive manufacturing types of equipment, including forming, sintering,
CNC machining, precision grinding, laser cutting, and so on, it helps us to control the quality very well.
Also, it greatly benefits cost control.


FAQs (Frequently Asked Questions)
Q1. Are you a factory or trading company?
A: We are a manufacturer of over 15 years of experience. You are welcome to visit our factory.

Q2: Do you send a sample to check?
A: Sure, the sample is free and freight collect.

Q3: When will you ship it?
A: If the products are in storage, we'll ship within 48 hours

Q4: When can I get the price?
A: We regularly quote within 24 hours after we get your inquiry. If you are in urgent need of getting the price.
Please call us or tell us in your email so that we will proceed with your inquiry as a priority.

Q5: Is it available to provide customized products?
A: We always support custom-made demand as per different materials, dimensions, and designs.