Yttria Stabilized Zro2 Sheet Crcuit Boards Zirconia Ceramic Plates Substrates

• Customization: Available
• Application: Electronic Devices, Lighting, Power Supply, Semiconductors
• Dielectric: Zirconia Ceramic
• Model NO.: JJBP-0121-0009
• Forming Method: Tape Casting
• Features: High Flexural Strength and Wear Resistance
• Usage: Blank Ceramic Circuit Board
• Optional Color: White, Yellow, Black, Blue
• Density: Over 6.0g/cm3
• Flexural Strength: >800MPa
• Dielectric Constant: 33MHz
• Dielectric Loss Angle: ≦16MHz
• Further Processing: CNC Machining, Fine Grinding
• Transport Package: Individual Package
• Specification: Standard or Customized
• Trademark: JingHui
• Origin: China
• HS Code: 8547100000

Product Description

Yttria Stabilized ZrO2 Sheet Crcuit Boards Zirconia Ceramic Plates Substrates


Product Introduction

Ceramic itself is a relatively brittle material, but because of the addition of zirconia, the toughness has been extremely improved. Due to the smooth 
surface advantage of ceramics, the friction coefficient is extremely low and it is not easy to wear. In addition, ceramics also have strong
corrosion resistance.

Zirconia ceramics have low thermal conductivity, but they have high hardness, good wear resistance and corrosion resistance, high toughness
and high temperature resistance.

It has a very high melting point and is one of the best refractory materials in nature, so it can be perfectly competent in some mobile facilities with frequent vibrations and ultra-high temperature working environments. For example, rail transit semiconductor low-power modules and aerospace generator modules.

 

Product Parameters
 

Zirconia Ceramic Substrate
Item	Unit	ZrO2
Mechanical Properties
Color	/	White
Density	g/cm^3	≥6
Water Absorption	%	0
Vickers Hardness (Load 4.9N)	Gpa	11
Young's Modulus	GPa	200
Flexural Strength	Mpa	>800
Fracture Toughness	MPa·m^1/2	5.0
Thermal Properties
Max. Service Temperature (Non-loading)	ºC	1000
CTE (Coefficient of Thermal Expansion) (20-800ºC)	1×10^-6/ºC	7.8
Thermal Shock Resistance	≥10 Times	No Crack
Thermal Conductivity (25ºC)	W/m·K	>3
Specific Heat (25ºC)	J/kg·K	460
Electrical Properties
Volume Resistivity (25ºC)	Ω·cm	≥10^13
Dielectric Strength	KV/mm	≥10
Dielectric Constant (25ºC, 1MHz )	(E)	33
Dielectric Loss Angle (25ºC, 1MHz )	×10^-4	≤16

Production Process

The molding process used for our zirconia ceramic substrates is tape casting. 



Why Choose Us

Specializing in the production of bare ceramic substrates, Jinghui Ceramic has 15 years of R&D experience. Our products have high cost performance and will definitely satisfy you.