0.15mm 0.25mm Zro2 PCB Board Zirconia Plate Tzp Ceramic Substrate

• Customization: Available
• Application: Electronic Devices, Lighting, Power Supply, Semiconductors, Refractory, Structure Ceramic, Industrial Ceramic, Functional Ceramic
• Material: Zirconia Ceramic
• Model NO.: JJBP-0121-0009
• Forming Method: Tape Casting
• Features: High Flexural Strength and Wear Resistance
• Usage: Blank Ceramic Circuit Board
• Optional Color: White, Yellow, Black, Blue
• Density: Over 6.0g/cm3
• Dielectric Constant: 33MHz
• Dielectric Loss Angle: ≦16MHz
• Flexural Strength: >800MPa
• Type: Ceramic Plates
• Transport Package: Individual Package
• Trademark: JingHui
• Origin: China
• HS Code: 8547100000

Product Description

0.15mm 0.25mm ZrO2 PCB Board Zirconia Plate TZP Ceramic Substrate


Specializing in the production of bare ceramic substrates, Jinghui Ceramic has 15 years of R&D experience. Our products have high cost performance and will definitely satisfy you.


Product Introduction

Zirconia ceramics have low thermal conductivity, but they have high hardness, good wear resistance and corrosion resistance, high toughness
and high temperature resistance.

It has a very high melting point and is one of the best refractory materials in nature, so it can be perfectly competent in some mobile facilities with frequent vibrations and ultra-high temperature working environments. For example, rail transit semiconductor low-power modules and aerospace generator modules.

 

Product Parameters
 

Zirconia Ceramic Substrate
Item	Unit	ZrO2
Mechanical Properties
Color	/	White
Density	g/cm^3	≥6
Water Absorption	%	0
Vickers Hardness (Load 4.9N)	Gpa	11
Young's Modulus	GPa	200
Flexural Strength	Mpa	>800
Fracture Toughness	MPa·m^1/2	5.0
Thermal Properties
Max. Service Temperature (Non-loading)	ºC	1000
CTE (Coefficient of Thermal Expansion) (20-800ºC)	1×10^-6/ºC	7.8
Thermal Shock Resistance	≥10 Times	No Crack
Thermal Conductivity (25ºC)	W/m·K	>3
Specific Heat (25ºC)	J/kg·K	460
Electrical Properties
Volume Resistivity (25ºC)	Ω·cm	≥10^13
Dielectric Strength	KV/mm	≥10
Dielectric Constant (25ºC, 1MHz )	(E)	33
Dielectric Loss Angle (25ºC, 1MHz )	×10^-4	≤16

Production Process

The forming process for our zirconia ceramic substrates is tape casting. 