Application: | Refractory, Structure Ceramic, Industrial Ceramic, Functional Ceramic |
---|---|
Type: | Ceramic Plates |
Forming Method: | Tape Casting |
Purity of Material: | 96%, 99.6% Alumina |
Features: | High Mechanical Strength, Small Dielectric Loss |
Usage: | Blank Ceramic Circuit Board |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
1. Product Specification
Products of various specifications can be produced. The table below shows our standard thicknesses and sizes.
Alumina Ceramic Substrate | |||||||
99.6% Al2O3 | |||||||
Thickness (mm) | Maximum Size (mm) | Shape | Molding Technique | ||||
As Fired | Lapped | Polished | Rectangular | Square | Round | ||
0.1-0.2 | 50.8 | 50.8 | √ | √ | Tape Casting | ||
0.25 | 114.3 | 114.3 | √ | Tape Casting | |||
0.38 | 120 | 114.3 | 114.3 | √ | Tape Casting | ||
0.5 | 120 | 114.3 | 114.3 | √ | Tape Casting | ||
0.635 | 120 | 114.3 | 114.3 | √ | Tape Casting | ||
Other special thicknesses within the thickness range of 0.1-0.635mm can be achieved by lapping. | |||||||
96% Al2O3 | |||||||
Thickness (mm) | Maximum Size (mm) | Shape | Molding Technique | ||||
As Fired | Lapped | Polished | Rectangular | Square | Round | ||
0.25 | 120 | 114.3 | 114.3 | √ | Tape Casting | ||
0.3 | 120 | 114.3 | 114.3 | √ | Tape Casting | ||
0.38 | 140×190 | √ | Tape Casting | ||||
0.5 | 140×190 | √ | Tape Casting | ||||
0.635 | 140×190 | √ | Tape Casting | ||||
0.76 | 130×140 | √ | Tape Casting | ||||
0.8 | 130×140 | √ | Tape Casting | ||||
0.89 | 130×140 | √ | Tape Casting | ||||
1 | 280×240 | √ | Tape Casting | ||||
1.5 | 165×210 | √ | Tape Casting | ||||
2 | 500×500 | √ | Tape Casting | ||||
Other special thicknesses within the thickness range of 0.1-2.0mm can be achieved by lapping. |
Alumina Ceramic Substrate | ||||
Item | Unit | 96% Al2O3 | 99.6% Al2O3 | |
Mechanical Properties | ||||
Color | / | / | White | Ivory |
Density | Drainage Method | g/cm3 | ≥3.70 | ≥3.95 |
Light Reflectivity | 400nm/1mm | % | 94 | 83 |
Flexural Strength | Three Point Bending | MPa | >350 | >500 |
Fracture Toughness | Indentation Method | MPa·m1/2 | 3.0 | 3.0 |
Vickers Hardness | Load 4.9N | GPa | 14 | 16 |
Young's Modulus | Stretching Method | GPa | 340 | 300 |
Water Absorption | % | 0 | 0 | |
Camber | / | Length‰ | T≤0.3: ≤5‰, Others: ≤3‰ | ≤3‰ |
Thermal Properties | ||||
Max. Service Temperature (Non-loading) | / | ºC | 1200 | 1400 |
CTE (Coefficient of Thermal Expansion) |
20-800ºC | 1×10-6/ºC | 7.8 | 7.9 |
Thermal Conductivity | 25ºC | W/m·K | >24 | >29 |
Thermal Shock Resistance | 800ºC | ≥10 Times | No Crack | No Crack |
Specific Heat | 25ºC | J/kg·k | 750 | 780 |
Electrical Properties | ||||
Dielectric Constant | 25ºC, 1MHz | / | 9.4 | 9.8 |
Dielectric Loss Angle | 25ºC, 1MHz | ×10-4 | ≤3 | ≤2 |
Volume Resistivity | 25ºC | Ω·cm | ≥1014 | ≥1014 |
Dielectric Strength | DC | KV/mm | ≥15 | ≥15 |
Jinghui Industry Ltd. is dedicated to producing high quality products. We do our best to ensure that any substrates supplied by Jinghui Industry Ltd. fully meet your performance expectations.