| Customization: | Available |
|---|---|
| Application: | Refractory, Electronics, Industrial Ceramic, Electrical Ceramic |
| Type: | Ceramic Insulator |
|
Still deciding? Get samples of US$ 5/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
1. Forming Method
There are mainly Dry Pressing, Hot Pressing, Isostatic Pressing, and Ceramic Injection Molding (CIM), each of which has its own advantages and disadvantages. We will choose the most suitable forming method on the basis of saving costs and ensuring quality.
2. Finishing Process
In order to achieve the precision of the product, most ceramic structural parts need further finishing treatment after the sintering process. The main finishing processes we use are machining (lapping, polishing...) and glazing.
3. Metallization Process
Metallization of ceramics refers to the creation of thin metal layers (films) on the surface of ceramics. After the surface of the ceramic material is metallized, it has both the characteristics of ceramics and the properties of metal.
Which Metallization Processes We Support?
Jinghui specializes in the production of metallized ceramic structural components, has rich experience in manufacturing precision ceramic parts, and is proficient in the surface metallization process of ceramic structural parts such as Mo-Mn method, electroless nickel plating method, silver firing method and W-Au method. Here we focus on the Mo-Mn method.
Introduction to Mo-Mn Method
The process of the Mo-Mn method is to coat a layer of metal powder (with Mo powder and Mn powder as the main raw materials) on the ceramic surface, and form a solidified and dense metallized layer through high-temperature sintering, thereby realizing the metallization of ceramics.
The brief process of Mo-Mn method is shown in the picture below.
Metallized ceramic structural parts obtained by the Mo-Mn method have the following characteristics:
1. High bonding strength, high air tightness, high reliability and good heat resistance.
2. The finished product has dual characteristics of ceramic and metal.
We can produce metallized ceramic structural parts of various specifications according to customers' drawings.
Product Applications
| Category | Property | Unit | 99.8% Al2O3 |
99.5% Al2O3 |
99% Al2O3 |
95% Al2O3 |
94.4% Al2O3 |
| Mechanical | Density | g/cm3 | ≥3.95 | ≥3.90 | ≥3.85 | ≥3.65 | ≥3.60 |
| Water absorption | % | 0 | 0 | 0 | 0 | 0 | |
| Vickers hardness | HV | 1700 | 1700 | 1700 | 1500 | 1500 | |
| Flexural strength | Mpa | ≥ 390 | ≥ 379 | ≥ 338 | ≥ 320 | ≥ 312 | |
| Compressive strength | Mpa | ≥ 2650 | ≥ 2240 | ≥ 2240 | ≥ 2000 | ≥ 2000 | |
| Fracture toughness | Mpam1/2 | 4-5 | 4-5 | 4-5 | 3-4 | 3-4 | |
| Thermal | Max. Service temperature (non-loading) |
ºC | 1750 | 1675 | 1600 | 1500 | 1500 |
| CTE (Coefficient of thermal expansion) 20-800ºC |
1×10-6/ºC | 6.5-8.2 | 6.5-8.0 | 6.2-8.0 | 5.0-8.0 | 5.0-8.0 | |
| Thermal shock | T (ºC) | ≥ 200 | ≥ 200 | ≥ 200 | ≥ 220 | ≥ 220 | |
| Thermal conductivity 25ºC |
W/(m·k) | 31 | 30 | 29 | 24 | 22.4 | |
| Specific heat | 1×103J/(kg·k) | 0.78 | 0.78 | 0.78 | 0.78 | 0.78 | |
| Electrical | Volume resistivity 25ºC |
ohm·cm | > 1×1014 | > 1×1014 | > 1×1014 | > 1×1014 | > 1×1014 |
| 300ºC | 1×1012 | 1×1012 | 8×1011 | 1012-1013 | 1012-1013 | ||
| 500ºC | 2×1012 | 5×1010 | 2×109 | 1×109 | 1×109 | ||
| Dielectric strength | KV/mm | 20 | 19 | 18 | 18 | 18 | |
| Dielectric constant (1Mhz) | (E) | 9.8 | 9.7 | 9.5 | 9.5 | 9.5 |
We are confident that we can fulfill your product requirements well. Welcome to order with drawings or samples, and look forward to becoming your reliable partner!