White Yttria Stabilized Zirconium Oxide Ceramic Plate Zirconia Ceramic Substrate

• Customization: Available
• Application: Electronic Devices, Semiconductors
• Material: Zirconia Ceramic
• Model NO.: JJBP-0121-0010
• Type: Ceramic Plates
• Density: Over 6.0g/cm3
• Optional Color: White, Yellow, Black, Blue
• Forming Method: Tape Casting
• Flexural Strength: >800MPa
• Dielectric Constant: 33MHz
• Dielectric Loss Angle: ≦16MHz
• Customized Service: OEM, ODM, Prototyping, Trial Order
• Feature: High Flexural Strength and Wear Resistance
• Transport Package: Individual Package
• Specification: Customized
• Trademark: JingHui
• Origin: China
• HS Code: 8547100000
• Production Capacity: 50000 Pieces/Month

Product Description

White Yttria Stabilized Zirconium Oxide Ceramic Plate Zirconia Ceramic Substrate


Introduction of Zirconia Ceramic Substrates

Jinghui Ceramic is a professional manufacturer of zirconia ceramic substrates. It provides one-stop services from molding to sintering to machining to finished products. Welcome to contact us.

Zirconia ceramics have high toughness, high flexural strength, high wear resistance, excellent thermal insulation properties and the thermal expansion coefficient close to that of steel. Zirconia ceramic substrates have obvious advantages, such as strong mechanical properties, high temperature resistance, corrosion resistance, low thermal conductivity, and high insulation.


Molding Technique of Zirconia Ceramic Substrates

At present, injection molding, dry pressing and tape casting are usually used to pruduce zirconia ceramic substrates.

(1) Injection molding is only suitable for forming thick substrates with thicknesses more than 1mm.
(2) Dry pressing often causes delamination of the green body due to uneven radial and axial pressure distribution during the molding process.
(3) Tape casting is suitable for producing thin ceramic substrates with thicknesses from 0.2mm to 3mm. The have the advantages of fast production speed, high degree of automation, uniform structure and good product quality.

The molding process used for our bare zirconia ceramic substrates is tape casting. Below is the process flow.

 

Product Parameters
 

Zirconia Ceramic Substrate
Item	Unit	ZrO2
Mechanical Properties
Color	/	White
Density	g/cm^3	≥6
Water Absorption	%	0
Vickers Hardness (Load 4.9N)	Gpa	11
Young's Modulus	GPa	200
Flexural Strength	Mpa	>800
Fracture Toughness	MPa·m^1/2	5.0
Thermal Properties
Max. Service Temperature (Non-loading)	ºC	1000
CTE (Coefficient of Thermal Expansion) (20-800ºC)	1×10^-6/ºC	7.8
Thermal Shock Resistance	≥10 Times	No Crack
Thermal Conductivity (25ºC)	W/m·K	>3
Specific Heat (25ºC)	J/kg·K	460
Electrical Properties
Volume Resistivity (25ºC)	Ω·cm	≥10^13
Dielectric Strength	KV/mm	≥10
Dielectric Constant (25ºC, 1MHz )	(E)	33
Dielectric Loss Angle (25ºC, 1MHz )	×10^-4	≤16

Product Inspection




Company Profile

Jinghui Ceramic is a professional manufacturer of zirconia ceramic substrates and has a complete and scientific quality management system. We strive for excellence in product quality, and high quality is our original intention.

1. Every detail is in place

Our products are well-detailed, have high surface finish and stable performance.

2. Quality control
Using testing equipment and manual screening to ensure that products reach customers without quality problems.

3. Technical support
We can customize as per customer requirements and can provide customers with reference solutions.

4. Fast shipping
The use of mechanized automatic production effectively improves production efficiency while saving labor costs.