1. Forming Method
There are mainly Dry Pressing, Hot Pressing, Isostatic Pressing, and Ceramic Injection Molding (CIM), each of which has its own advantages and disadvantages. We will choose the most suitable forming method on the basis of saving costs and ensuring quality.
2. Finishing Process
In order to achieve the precision of the product, most ceramic structural parts need further finishing treatment after the sintering process. The main finishing processes we use are machining (lapping, polishing...) and glazing.
3. Metallization Process
Metallization of ceramics refers to the creation of thin metal layers (films) on the surface of ceramics. After the surface of the ceramic material is metallized, it has both the characteristics of ceramics and the properties of metal.
Which Metallization Processes We Support?
Jinghui specializes in the production of metallized ceramic structural components, has rich experience in manufacturing precision ceramic parts, and is proficient in the surface metallization process of ceramic structural parts such as Mo-Mn method, electroless nickel plating method, silver firing method and W-Au method. Here we focus on the Mo-Mn method.
Introduction to Mo-Mn Method
The simple mechanism of Mo-Mn method is: Mo powder and Mn powder are used as the main raw materials, and a certain amount of other metal powders are added, as well as metal oxides as active agents (such as Al2O3, MgO, SiO2, CaO, etc.), sintered at high temperature in a reducing atmosphere to form a Mo layer. To prevent oxidation and improve wettability, after the metallized Mo layer is sintered, a layer of Ni can be plated on it.
The brief process of Mo-Mn method is shown in the picture below.
Metallized ceramic structural parts obtained by the Mo-Mn method have the following characteristics:
1. High bonding strength, high air tightness, high reliability and good heat resistance.
2. The finished product has dual characteristics of ceramic and metal.
We can produce metallized ceramic structural parts of various specifications according to customers' drawings.
Product Applications
| Category | Property | Unit | 99.8% Al2O3 |
99.5% Al2O3 |
99% Al2O3 |
95% Al2O3 |
94.4% Al2O3 |
| Mechanical | Density | g/cm3 | ≥3.95 | ≥3.90 | ≥3.85 | ≥3.65 | ≥3.60 |
| Water absorption | % | 0 | 0 | 0 | 0 | 0 | |
| Vickers hardness | HV | 1700 | 1700 | 1700 | 1500 | 1500 | |
| Flexural strength | Mpa | ≥ 390 | ≥ 379 | ≥ 338 | ≥ 320 | ≥ 312 | |
| Compressive strength | Mpa | ≥ 2650 | ≥ 2240 | ≥ 2240 | ≥ 2000 | ≥ 2000 | |
| Fracture toughness | Mpam1/2 | 4-5 | 4-5 | 4-5 | 3-4 | 3-4 | |
| Thermal | Max. Service temperature (non-loading) |
ºC | 1750 | 1675 | 1600 | 1500 | 1500 |
| CTE (Coefficient of thermal expansion) 20-800ºC |
1×10-6/ºC | 6.5-8.2 | 6.5-8.0 | 6.2-8.0 | 5.0-8.0 | 5.0-8.0 | |
| Thermal shock | T (ºC) | ≥ 200 | ≥ 200 | ≥ 200 | ≥ 220 | ≥ 220 | |
| Thermal conductivity 25ºC |
W/(m·k) | 31 | 30 | 29 | 24 | 22.4 | |
| Specific heat | 1×103J/(kg·k) | 0.78 | 0.78 | 0.78 | 0.78 | 0.78 | |
| Electrical | Volume resistivity 25ºC |
ohm·cm | > 1×1014 | > 1×1014 | > 1×1014 | > 1×1014 | > 1×1014 |
| 300ºC | 1×1012 | 1×1012 | 8×1011 | 1012-1013 | 1012-1013 | ||
| 500ºC | 2×1012 | 5×1010 | 2×109 | 1×109 | 1×109 | ||
| Dielectric strength | KV/mm | 20 | 19 | 18 | 18 | 18 | |
| Dielectric constant (1Mhz) | (E) | 9.8 | 9.7 | 9.5 | 9.5 | 9.5 |