High Purity Laser Scribing Aluminum Oxide Al2O3 Alumina Ceramic Sheet

Product Description

High Purity Laser Scribing Aluminum Oxide Al2O3 Alumina Ceramic Sheet

Product Introduction

Advantages of Laser Scribing

Due to the special properties of alumina ceramic sheets, they generally cannot be processed by traditional processing techniques, and we generally need to use lasers for processing.

Laser scribing has high precision, fast speed, no scratch on the workpiece and no mechanical deformation, and can process any graphics.

Product Parameters

Alumina Ceramic Sheet
Item	Unit		96% Al2O3	99.6% Al2O3
Mechanical Properties
Color	/	/	White	Ivory
Density	Drainage Method	g/cm^3	≥3.70	≥3.95
Light Reflectivity	400nm/1mm	%	94	83
Flexural Strength	Three Point Bending	MPa	>350	>500
Fracture Toughness	Indentation Method	MPa·m^1/2	3.0	3.0
Vickers Hardness	Load 4.9N	GPa	14	16
Young's Modulus	Stretching Method	GPa	340	300
Water Absorption		%	0	0
Camber	/	Length‰	T≤0.3: ≤5‰, Others: ≤3‰	≤3‰
Thermal Properties
Max. Service Temperature (Non-loading)	/	ºC	1200	1400
CTE (Coefficient of Thermal Expansion)	20-800ºC	1×10^-6/ºC	7.8	7.9
Thermal Conductivity	25ºC	W/m·K	>24	>29
Thermal Shock Resistance	800ºC	≥10 Times	No Crack	No Crack
Specific Heat	25ºC	J/kg·k	750	780
Electrical Properties
Dielectric Constant	25ºC, 1MHz	/	9.4	9.8
Dielectric Loss Angle	25ºC, 1MHz	×10^-4	≤3	≤2
Volume Resistivity	25ºC	Ω·cm	≥10^14	≥10^14
Dielectric Strength	DC	KV/mm	≥15	≥15

Manufacturing Capacity

1. Laser Processing

(1) Hole Size

Alumina Ceramic Sheet
Hole Diameter (mm)	Standard Tolerance (mm)
φ≤0.5	0.08
φ>0.5	0.2

(2) Laser Scribing
 

Alumina Ceramic Sheet
Substrate Thickness (mm)	the Percentage of Laser Scribe Line Depth to Thickness (%)
0.2-0.3	40%±5%
0.3<T≤0.5	50%±3%
0.5<T≤1.0	43%±3%
1.2	55%±3%
1.5	55%±3%
2.0	55%+10%
The scribing spot can be in different sizes. Generally there are small spot 0.03-0.04mm (Substrate Thickness≤0.5mm ) and large spot 0.08-0.1mm (Substrate Thickness>0.5mm), and the accuracy is ±0.01mm.

2. Product Specification

The table below shows our standard sizes. We can also customize the size according to your requirements.

Alumina Ceramic Sheet
99.6% Al2O3
Thickness (mm)	Maximum Size (mm)			Shape			Molding Technique
	As Fired	Lapped	Polished	Rectangular	Square	Round
0.1-0.2		50.8	50.8		√	√	Tape Casting
0.25		114.3	114.3		√		Tape Casting
0.38	120	114.3	114.3		√		Tape Casting
0.5	120	114.3	114.3		√		Tape Casting
0.635	120	114.3	114.3		√		Tape Casting
Other special thicknesses within the thickness range of 0.1-0.635mm can be achieved by lapping.
96% Al2O3
Thickness (mm)	Maximum Size (mm)			Shape			Molding Technique
	As Fired	Lapped	Polished	Rectangular	Square	Round
0.25	120	114.3	114.3		√		Tape Casting
0.3	120	114.3	114.3		√		Tape Casting
0.38	140×190			√			Tape Casting
0.5	140×190			√			Tape Casting
0.635	140×190			√			Tape Casting
0.76	130×140			√			Tape Casting
0.8	130×140			√			Tape Casting
0.89	130×140			√			Tape Casting
1	280×240			√			Tape Casting
1.5	165×210			√			Tape Casting
2	500×500			√			Tape Casting
Other special thicknesses within the thickness range of 0.1-2.0mm can be achieved by lapping.

3. Product Tolerances
 

Alumina Ceramic Sheet
Item	Substrate Thickness (mm)	Standard Tolerance (mm)	Best Tolerance (mm)	Laser Cutting Tolerance (mm)
Length and Width Tolerance	/	±2		±0.15
Thickness Tolerance	T<0.3	±0.03	±0.01
	0.30-1.0	±0.05	±0.01
	T>1.0	±10%	±0.01

4. Surface Roughness
 

Alumina Ceramic Sheet
Material	Surface Roughness (μm)
	As Fired	Lapped	Polished
96% Al2O3	Ra 0.2-0.75	Ra 0.3-0.7	Ra ≤0.05
99.6% Al2O3	Ra 0.05-0.15	Ra 0.1-0.5	Ra ≤0.05

Applications