| Application: | Electronics, Refractory, Structure Ceramic, Industrial Ceramic |
|---|---|
| Type: | Ceramic Part |
| Product Name: | Metallized Ceramics |
| Optional Purity: | 94.4%-99.8% Alumina |
| Color: | White, Beige, Pink |
| Further Finishing Treatment: | Machining, Glazing, etc |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier Jinghui Ceramic produces a variety of high-purity alumina metallized ceramics. The products are mainly used in high-voltage and high-current applications. The industry fields include vacuum electronics, medical care, new energy vehicles, and aerospace.
Our alumina metallized ceramics generally use 95%, 99% or 99.5% alumina. We can produce a variety of custom ceramic parts to suit different applications. At the same time, we metallize designated areas of the part so that the ceramic can subsequently be brazed to the metal component.
Our production process is mainly divided into 3 steps, forming - finishing - metallization. The production flow chart is shown below.
1. Forming Method / Molding Craft
There are mainly Dry Pressing, Hot Pressing, Isostatic Pressing, and Ceramic Injection Molding (CIM), each of which has its own advantages and disadvantages. We will choose the most suitable forming method on the basis of saving costs and ensuring quality.
2. Finishing Process
In order to achieve the precision of the product, most ceramic structural parts need further finishing treatment after the sintering process. The main finishing processes we use are machining (lapping, polishing...) and glazing.
3. Metallization Process
Metallization of ceramics refers to the creation of thin metal layers (films) on the surface of ceramics. After the surface of the ceramic material is metallized, it has both the characteristics of ceramics and the properties of metal.
Below is the data sheet of our alumina ceramic materials.
| Category | Property | Unit | 99.8% Al2O3 |
99.5% Al2O3 |
99% Al2O3 |
95% Al2O3 |
94.4% Al2O3 |
| Mechanical | Density | g/cm3 | ≥3.95 | ≥3.90 | ≥3.85 | ≥3.65 | ≥3.60 |
| Water absorption | % | 0 | 0 | 0 | 0 | 0 | |
| Vickers hardness | HV | 1700 | 1700 | 1700 | 1500 | 1500 | |
| Flexural strength | Mpa | ≥ 390 | ≥ 379 | ≥ 338 | ≥ 320 | ≥ 312 | |
| Compressive strength | Mpa | ≥ 2650 | ≥ 2240 | ≥ 2240 | ≥ 2000 | ≥ 2000 | |
| Fracture toughness | Mpam1/2 | 4-5 | 4-5 | 4-5 | 3-4 | 3-4 | |
| Thermal | Max. Service temperature (non-loading) |
ºC | 1750 | 1675 | 1600 | 1500 | 1500 |
| CTE (Coefficient of thermal expansion) 20-800ºC |
1×10-6/ºC | 6.5-8.2 | 6.5-8.0 | 6.2-8.0 | 5.0-8.0 | 5.0-8.0 | |
| Thermal shock | T (ºC) | ≥ 200 | ≥ 200 | ≥ 200 | ≥ 220 | ≥ 220 | |
| Thermal conductivity 25ºC |
W/(m·k) | 31 | 30 | 29 | 24 | 22.4 | |
| Specific heat | 1×103J/(kg·k) | 0.78 | 0.78 | 0.78 | 0.78 | 0.78 | |
| Electrical | Volume resistivity 25ºC |
ohm·cm | > 1×1014 | > 1×1014 | > 1×1014 | > 1×1014 | > 1×1014 |
| 300ºC | 1×1012 | 1×1012 | 8×1011 | 1012-1013 | 1012-1013 | ||
| 500ºC | 2×1012 | 5×1010 | 2×109 | 1×109 | 1×109 | ||
| Dielectric strength | KV/mm | 20 | 19 | 18 | 18 | 18 | |
| Dielectric constant (1Mhz) | (E) | 9.8 | 9.7 | 9.5 | 9.5 | 9.5 |
Jinghui Ceramic has rich experience in manufacturing precision ceramic parts, and is proficient in the surface metallization process of ceramic structural parts such as Mo-Mn metallization, electroless nickel plating method, silver metallization and DBC technology. If you're interested, you can reply to us for more info.