96% Alumina Ceramic Insulating Plate Precision Machining Supported Al2O3 Substrate

• Standard: GB, ISO 9001
• Application: Blank Ceramic Circuit Board
• Material: 96% Alumina Ceramic
• Type: Ceramic Substrate
• Forming Method: Tape Casting
• Features: High Mechanical Strength, Small Dielectric Loss
• Model NO.: JJBP-0111-0011
• Optional Color: White, Ivory, Pink, Black
• Density: Over 3.70g/cm3
• Standard Thickness: 0.25-2.0mm Available
• Thickness Tolerance: ±0.03/0.05mm (Depending on Thickness)
• Length and Width Tolerance: ±2mm
• Transport Package: Individual Package
• Specification: Max. up to 500mm x 500mm
• Trademark: JingHui
• Origin: China
• HS Code: 8547100000

Product Description

96% Alumina Ceramic Insulating Plate Precision Machining Supported Al2O3 Substrate

Product Introduction

Shape of the Alumina Ceramic Substrate

Our as fired bare alumina ceramic substrates are often rectangular or square in shapes.

Size of the Alumina Ceramic Substrate

The size of the alumina ceramic substrate is not the bigger the better, mainly because the base material is made of ceramics, and it is easy to cause the substrate to break during the PCB proofing process, resulting in a lot of waste.

Our standard thicknesses for as-fired 96% alumina ceramic substrates are 0.25mm, 0.30mm, 0.38mm, 0.50mm, 0.635mm, 0.76mm, 0.80mm, 0.89mm, 1.0mm, 1.5mm and 2.0mm.

Product Parameters

Alumina Ceramic Substrate
Item	Unit		96% Al2O3
Mechanical Properties
Color	/	/	White
Density	Drainage Method	g/cm^3	≥3.70
Light Reflectivity	400nm/1mm	%	94
Flexural Strength	Three Point Bending	MPa	>350
Fracture Toughness	Indentation Method	MPa·m^1/2	3.0
Vickers Hardness	Load 4.9N	GPa	14
Young's Modulus	Stretching Method	GPa	340
Water Absorption		%	0
Camber	/	Length‰	T≤0.3: ≤5‰, Others: ≤3‰
Thermal Properties
Max. Service Temperature (Non-loading)	/	ºC	1200
CTE (Coefficient of Thermal Expansion)	20-800ºC	1×10^-6/ºC	7.8
Thermal Conductivity	25ºC	W/m·K	>24
Thermal Shock Resistance	800ºC	≥10 Times	No Crack
Specific Heat	25ºC	J/kg·k	750
Electrical Properties
Dielectric Constant	25ºC, 1MHz	/	9.4
Dielectric Loss Angle	25ºC, 1MHz	×10^-4	≤3
Volume Resistivity	25ºC	Ω·cm	≥10^14
Dielectric Strength	DC	KV/mm	≥15

Applications

Production Process

The molding process used for our alumina ceramic substrates is tape casting.